Data sheet

Durethan BKV50 000000
PA 6, 50 % glass fibers, injection molding
ISO Shortname:ISO 16396-PA 6,GF50,GR,S14-160
Property Test Condition Unit Standard guide value
d.a.m。 cond.
Rheological properties
Molding shrinkage, parallel 150x105x3; 280 °C / MT 80 °C; 400 bar % acc. ISO 2577 0.16
Molding shrinkage, transverse 150x105x3; 280 °C / MT 80 °C; 400 bar % acc. ISO 2577 0.85
Post- shrinkage, parallel 150x105x3; 120 °C; 4 h % acc. ISO 2577 0.02
Post- shrinkage, transverse 150x105x3; 120 °C; 4 h % acc. ISO 2577 0.05

Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 16300 9800
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 220 145
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 3.0 5.0
C Tensile creep modulus 1 h MPa ISO 899-1 8100
C Tensile creep modulus 1000 h MPa ISO 899-1 6600
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 100 110
C Charpy impact strength -30 °C kJ/m² ISO 179-1eU 85 85
C Charpy notched impact strength 23 °C kJ/m² ISO 179-1eA 20 25
C Charpy notched impact strength -30 °C kJ/m² ISO 179-1eA 15 15
Izod notched impact strength 23 °C kJ/m² ISO 180-1A 20 25
Izod notched impact strength -30 °C kJ/m² ISO 180-1A 13 14
Flexural modulus 2 mm/min MPa ISO 178-A 15100 9700
Flexural strength 2 mm/min MPa ISO 178-A 365 235
Flexural strain at flexural strength 2 mm/min % ISO 178-A 3.0 5.0
Flexural stress at 3.5 % strain 2 mm/min MPa ISO 178-A 210
C Puncture energy 23 °C J ISO 6603-2 9 14
C Puncture energy -30 °C J ISO 6603-2 6
Ball indentation hardness N/mm² ISO 2039-1 270 135

Thermal properties
C Melting temperature 10 °C/min °C ISO 11357-1,-3 222
C Temperature of deflection under load 1.80 MPa °C ISO 75-1,-2 205
C Temperature of deflection under load 0.45 MPa °C ISO 75-1,-2 215
Vicat softening temperature 50 N; 120 °C/h °C ISO 306 > 200
C Coefficient of linear thermal expansion, parallel 23 to 55 °C 10-4/K ISO 11359-1,-2 0.2
C 线性热膨胀系数,transverse 23 to 55 °C 10-4/K ISO 11359-1,-2 0.7
C Burning behavior UL 94 1.5 mm Class UL 94 HB
C Oxygen index Method A % ISO 4589-2 24
Glow wire test (GWFI) 2.0 mm °C IEC 60695-2-12 650

Electrical properties (23 °C/50 % r. h.)
C Relative permittivity 100 Hz - IEC 60250 4.0
C Relative permittivity 1 MHz - IEC 60250 4.0 5.0
C Dissipation factor 100 Hz 10-4 IEC 60250 100
C Dissipation factor 1 MHz 10-4 IEC 60250 150 1400
C Volume resistivity Ohm·m IEC 60093 1E13 1E10
C Surface resistivity Ohm IEC 60093 1E14 1E12
C Electric strength 1 mm kV/mm IEC 60243-1 40 35
C Comparative tracking index CTI Solution A Rating IEC 60112 525

Other properties (23 °C)
C Water absorption (Saturation value) Water at 23 °C % ISO 62 5.0
C Water absorption (Equilibrium value) 23 °C; 50 % RH % ISO 62 1.5
C Density kg/m³ ISO 1183 1570
Bulk density kg/m³ ISO 60 700

Processing conditions for test specimens
C Injection molding-Melt temperature °C ISO 294 280
C Injection molding-Mold temperature °C ISO 294 80

Processing recommendations
Drying temperature dry air dryer °C - 80
Drying time dry air dryer h - 2-6
Residual moisture content % Acc. to Karl Fischer 0.03-0.12
Melt temperature (Tmin - Tmax) °C - 270-290
Mold temperature °C - 80-120
C These property characteristics are taken from the CAMPUS plastics data bank and are based on the international catalogue of basic data for plastics according to ISO 10350.
Disclaimer
Disclaimer for commercial products
This information and our technical advice - whether verbal, in writing or by way of trials - are given in good faith but without warranty, and this also applies where proprietary rights of third parties are involved. Our advice does not release you from the obligation to verify the information currently provided - especially that contained in our safety data and technical information sheets - and to test our products as to their suitability for the intended processes and uses. The application, use and processing of our products and the products manufactured by you on the basis of our technical advice are beyond our control and, therefore, entirely your own responsibility. Our products are sold in accordance with the current version of our General Conditions of Sale and Delivery.
Test values
Unless specified to the contrary, the values given have been established on standardized test specimens at room temperature. The figures should be regarded as guide values only and not as binding minimum values. Kindly note that, under certain conditions, the properties can be affected to a considerable extent by the design of the mould/die, the processing conditions and the coloring.
Processing note
Under the recommended processing conditions small quantities of decomposition product may be given off during processing. To preclude any risk to the health and well-being of the machine operatives, tolerance limits for the work environment must be ensured by the provision of efficient exhaust ventilation and fresh air at the workplace in accordance with the Safety Data Sheet. In order to prevent the partial decomposition of the polymer and the generation of volatile decomposition products, the prescribed processing temperatures should not be substantially exceeded. Since excessively high temperatures are generally the result of operator error or defects in the heating system, special care and controls are essential in these areas.
Conditioning
Conditioning in accordance with ISO 1110 (70 °C; 62 % r.h.)
LANXESSDEUTSCHLAND GMBH|D-50569 COLOGNE
Date: 2021-08-13 15:51:12.0
© LANXESS, 2014. All rights reserved. Your use of this site is subject to our terms of use.