Data sheet

Durethan BC304 000000
PA 6, non-reinforced, injection molding, improved impact strength
ISO/ASTM
ISO Shortname:ISO 16396-PA 6-I,,GR,S14-020
Property Test Condition Unit Standard guide value1
d.a.m。 cond.
Rheological properties
Molding shrinkage, parallel 150x105x3; 270 °C / WZ 80 °C; 500 bar % acc. ISO 2577 1.14
Molding shrinkage, transverse 150x105x3; 270 °C / WZ 80 °C; 500 bar % acc. ISO 2577 1.45
Post- shrinkage, parallel 150x105x3; 120 °C; 4 h % acc. ISO 2577 0.38
Post- shrinkage, transverse 150x105x3; 120 °C; 4 h % acc. ISO 2577 0.46
C Molding shrinkage, parallel 60x60x2; 270 °C / WZ 80 °C; 600 bar % ISO 294-4 1.3
C Molding shrinkage, transverse 60x60x2; 270 °C / WZ 80 °C; 600 bar % ISO 294-4 1.4
Post- shrinkage, parallel 60x60x2; 120 °C; 4 h % ISO 294-4 0.1
Post- shrinkage, transverse 60x60x2; 120 °C; 4 h % ISO 294-4 0.15

Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1毫米/min MPa ISO 527-1,-2 1800 800
C Yield stress 50 mm/min MPa ISO 527-1,-2 45 35
C Yield strain 50 mm/min % ISO 527-1,-2 4.5 30
C Nominal strain at break 50 mm/min % ISO 527-1,-2 > 50 > 50
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU N N
C Charpy impact strength -30 °C kJ/m² ISO 179-1eU N N
C Charpy notched impact strength 23 °C kJ/m² ISO 179-1eA 85 120
C Charpy notched impact strength -30 °C kJ/m² ISO 179-1eA 20 20
Izod notched impact strength 23 °C kJ/m² ISO 180-1A 70 100
Izod notched impact strength -30 °C kJ/m² ISO 180-1A 30 17
Flexural modulus 2 mm/min MPa ISO 178-A 1600 700
Flexural strength 2 mm/min MPa ISO 178-A 60 30
Flexural strain at flexural strength 2 mm/min % ISO 178-A 7.0 9.0
Flexural stress at 3.5 % strain 2 mm/min MPa ISO 178-A 55 25
C Puncture maximum force 23 °C N ISO 6603-2 4100
C Puncture maximum force -30 °C N ISO 6603-2 4800
C Puncture energy 23 °C J ISO 6603-2 55
C Puncture energy -30 °C J ISO 6603-2 60
Ball indentation hardness N/mm² ISO 2039-1 80 35

热性能
C Melting temperature 10 °C/min °C ISO 11357-1,-3 222
C Temperature of deflection under load 1.80 MPA °C ISO 75-1,-2 50
C Temperature of deflection under load 0.45 MPa °C ISO 75-1,-2 90
C Temperature of deflection under load 8.00 MPa °C ISO 75-1,-2 40
Vicat softening temperature 50 N; 120 °C/h °C ISO 306 150
C Coefficient of linear thermal expansion, parallel 23 to 55 °C 10-4/K ISO 11359-1,-2 1.5
C 线性热膨胀系数,transverse 23 to 55 °C 10-4/K ISO 11359-1,-2 1.6
C Burning behavior UL 94 1.5 mm Class UL 94 HB
C Oxygen index Method A % ISO 4589-2 21
Resistance to heat (ball pressure test) °C IEC 60695-10-2 194
Glow wire test (GWFI) 2.0 mm °C IEC 60695-2-12 650
燃烧行为US-FMVSSSS302 >=1.0 mm ISO 3795 passed
C Vicat softening temperature 50 N; 50 °C/h °C ISO 306 150

Electrical properties (23 °C/50 % r. h.)
C Relative permittivity 100Hz - IEC 60250 3.3 11
C Relative permittivity 1 MHz - IEC 60250 3.0 3.5
C Dissipation factor 100Hz 10-4 IEC 60250 70 1750
C Dissipation factor 1 MHz 10-4 IEC 60250 150 900
C Volume resistivity Ohm·m IEC 60093 1E13 1E10
C Surface resistivity Ohm IEC 60093 1E15 1E14
C Electric strength 1毫米 kV/mm IEC 60243-1 35 35
C Comparative tracking index CTI Solution A Rating IEC 60112 600
Comparative tracking index CTI M Solution B Rating IEC 60112 600 M

其他特性（23°C）
C Water absorption (Saturation value) Water at 23 °C % ISO 62 7.5
C Water absorption (Equilibrium value) 23 °C; 50 % RH % ISO 62 2.2
C Density kg/m³ ISO 1183 1060
Bulk density kg/m³ ISO 60 600

Processing conditions for test specimens
C Injection molding-Melt temperature °C ISO 294 270
C Injection molding-Mold temperature °C ISO 294 80

Processing recommendations
Drying temperature dry air dryer °C - 80
Drying time dry air dryer h - 2-6
Residual moisture content % Acc. to Karl Fischer 0.03-0.12
Melt temperature (Tmin - Tmax) °C - 260-280
Mold temperature °C - 80-90

Notes
1 Typical properties: these are not to be construed as specifications
C These property characteristics are taken from the CAMPUS plastics data bank and are based on the international catalogue of basic data for plastics according to ISO 10350.
Disclaimer
Disclaimer for commercial products
This information and our technical advice - whether verbal, in writing or by way of trials - are given in good faith but without warranty, and this also applies where proprietary rights of third parties are involved. Our advice does not release you from the obligation to verify the information currently provided - especially that contained in our safety data and technical information sheets - and to test our products as to their suitability for the intended processes and uses. The application, use and processing of our products and the products manufactured by you on the basis of our technical advice are beyond our control and, therefore, entirely your own responsibility. Our products are sold in accordance with the current version of our General Conditions of Sale and Delivery.
Test values
Unless specified to the contrary, the values given have been established on standardized test specimens at room temperature. The figures should be regarded as guide values only and not as binding minimum values. Kindly note that, under certain conditions, the properties can be affected to a considerable extent by the design of the mould/die, the processing conditions and the coloring.
Processing note
在推荐的处理条件下，在处理过程中可能会发出少量分解产物。为了排除机器操作员的健康和福祉的任何风险，必须通过安全数据表在工作场所提供有效的排气通风和新鲜空气来确保对工作环境的公差限制。为了防止聚合物的部分分解和挥发性分解产物的产生，不应基本上超过规定的加工温度。由于高温过高通常是供暖系统中操作员错误或缺陷的结果，因此在这些区域中，特殊护理和控制是必不可少的。
Conditioning
Conditioning in accordance with ISO 1110 (70 °C; 62 % r.h.)
LANXESSPerformance Materials GmbH|DE 50569 COLOGNE|Germany
Date: 2022-03-01 10:58:26.0